Product Details:
|
| Product Name: | J301 PU Adhesive | Color: | White To Pale Yellow Fluid And Dark Brown |
|---|---|---|---|
| Component: | A And B | State: | Fluid And Liquid |
| Applications: | Building | Advantage: | High Strength |
| MOQ: | 50kg | Package: | Plastic Bottle |
| Payment Mothed: | T/T, Paypal | Leading Time: | 7-15 Working Days |
| High Light: | J301 PU Based Adhesive,ISO9001 PU Based Adhesive,J301 2 Part PU Adhesive |
||
J301 Polyurethane Adhesive For Automobile Manufacturing Industry
1. Descriptions:
J301 is a two-component adhesive. Component A is composed of a variety of polyols, adhesion enhancers and fillers, and the appearance is light yellow red viscous fluid. Component B is composed of coarse MDI, which is brownish yellow transparent viscous liquid.
The PU adhesive is mainly used for bonding honeycomb board and corrugated board products. After bonding, honeycomb board can be sprayed through the production line, and can also be used for composite bonding for decoration of all kinds of metals, wood, porcelain chips, polished bricks, stones and so on.
2. Specifications:
| PU Adhesive | |
| Component A | White to pale yellow fluid slightly change |
| Component B | Dark brown liquid |
| A: Density (g/cm3) | 1.56 |
| B: Density (g/cm3) | 1.21 |
| A: State | Fluid |
| B: State | Liquid |
| Shearing Strength | ≥18MPa |
| Mixing ratio | 5:01 |
| Initialadhesive formation | 5-8 hours |
| Rollerpeel strength | ≥72(N.mm)/mm |
| Features | Cost-effective polyurethane adhesive with high hardness and high initial adhesion for indoor, better machanical behavior, special for railway |
| Technical Parameters ( tested under 20-25°C) | |||
| Item | Component A | Component B | After Mixing |
| Color | yellow to yellowish red | brownish yellow | Off-white |
| Density (g/cm3) | 1.30±0.02 | 1.00±0.02 | 1.15±0.1 |
| State | Fluid | Fluid | Fluid |
| Mixing ratio | 5:01 | ||
| After Mixing | |||
| Work life(100g) | 50-60 mins | ||
| Recommended operating time | within 35mins (from mixing to finishing) | ||
| Temperature Range for application | 15-35°C,45% humidity | ||
| Initial Bonding | 5-6 hours at 25°C / 60mins at 65°C | ||
| Time to reach full cure | 1-2 days under room temperature | ||
| / 24 hours at 60°C keep 60mins | |||
| Shearing Strength | ≥13MPa (60mins at 60°C or 3 days at 25°C) | ||
| VOC Test | Accord with GB18538 /TB3139 | ||
| Flame Retardant Rating | S4 (DIN5510) | ||
3. PU Adhesive has several advantages:
• Good flexibility
• High bonding strength
• Cost-effective
• Water and heat resistant
4. Applications:
• BEECORE Polyurethane composite adhesives are widely used in the construction industry, automobile manufacturing and shipbuilding, such as polyurethane sandwich panels, aluminum honeycomb panels, polystyrene foam panels, fiberglass panels, stone composite panels, metal plates, etc.
5. Quality control:
A very technical engineering team. The general manager has worked in the Netherlands. The core technologies are introduced from the Netherlands. Others are very young and have more than 5 years of practical experience.
Strict QC team: 8 people are responsible for PU Adhesive of quality control of parts, processing, testing, packaging, etc.
6. PU Adhesive of more pictures:
7. Company profile
Suzhou Beecore Honeycomb Materials Co.Ltd, originated from Besin (Dutch) International Group which was founded in 1957. It is the world's leading professional manufacturer of honeycomb materials. Since it' s established, the company has been committed to the research and development of honeycomb technology, from slant-porous aluminum honeycomb core, honeycomb core, honeycomb panel, to the finished product which was using honeycomb panel as the solution, such as truck body, laser TV / projection screen etc. , We always stick to the roots of continuous technological innovation, and constantly upgrade and expand the application of the honeycomb materials, becoming the first choice company for solutions of honeycomb materials.
At present, we hold more than 60% market share in the Yangtze River Delta of China. The overseas market covers Europe, America, Middle East, Southeast Asia and other countries, praised by domestic and foreign customers.
1958 Besin brought honeycomb technology into China, and Besin (Suzhou) company was established.
2002 Beecore (Guangdong) factory was established and have 10 aluminum honeycomb production lines.
2009 Suzhou Beecore Honeycomb Materials Co., Ltd was established and mainly produce aluminum honeycomb core and paper honeycomb core and other products.
2010 Beecore products are widely used for railway industry, Shanghai Expo, marine furniture etc.
2014 Beecore developed micro-porous aluminum honeycomb core and slant-porous aluminum honeycomb core, PU adhesive, as well as honeycomb filters.
2015 Beecore added honeycomb panels production lines, specialized in super length, width, curved, and special honeycomb panels of industry field.
2016 The self-developed aluminum honeycomb equipment has been exported to Europe, America, Asia and already obtained the technology patent in China.
2017- so far Suzhou Beecore Honeycomb Materials Co., Ltd is honored as the high-technology innovation enterprise.
9. Matters needing attention:
1. The amount of glue should not be too much to avoid accelerating curing and shortening the application period due to exothermic reaction.
2. There shall be absolutely no water during bonding. Grinding the bonded surface can increase the bonding strength, while epoxy primer on the bonded metal surface can increase the bonding.
The surface to be bonded and coated after pretreatment shall be dry and free of grease, dust or other dirt. If the metal surface is coated with primer or the plastic surface has discharge agent, it shall be removed; The bonded surface is polished. In some special cases, epoxy primer or anodic oxidation may be used, and the adhesion will increase significantly.
For construction and bonding J301, take an appropriate amount of glue solution according to the mass ratio a: B = 5:1, stir and mix evenly (based on the uniform mixing of the colors of glue solution a and b), and then coat, scrape and trowel the evenly stirred colloid on the required plate with a scraper, with the glue application amount of 0.35-0.5kg per square meter.
After mixing, J301 can be mixed evenly at room temperature for about 50 ~ 60 minutes, and the initial curing time at 25 ℃ is about 6 ~ 7 hours. If the temperature is low, the curing time needs to be prolonged. It can also be cured quickly by heating. Generally, it can be basically cured after 1 hour at 60 ℃.
The uncured glue can be cleaned with special cleaning agent, such as acetone. The cured glue can only be removed by mechanical method.
Preservation:
Afraid of freezing: Yes
Storage temperature: at room temperature (recommendation: about 25 ℃), when the storage temperature is too high, the reaction speed is fast and the operation time is short after taking and mixing; The temperature is too low, the viscosity is thickened, and the glue mixing and scraping are laborious.
Validity: 12 months after the original packaging
Packing:
Barrel packing: 25kg (group A), 5kg (group B) can be packed according to the specific requirements of customers
10. FAQ
Q1. What is PU adhesive used for?
A: Polyurethane composite adhesives are widely used in the construction industry, automobile manufacturing and shipbuilding, such as polyurethane sandwich panels, aluminum honeycomb panels, polystyrene foam panels, fiberglass panels, stone composite panels, metal plates, etc.
Q2. What are the advantages of PU adhesive?
A: PU adhesive has the advantages of good flexibility, high bonding strength, cost-effective, water and heat resistant
Q3. What is the packaging method of PU adhesive?
A: PU adhesive of samples are packed in cardboard and bulk orders are packed in plywood cases.
Contact Person: Stella Li
Tel: +8618362561302
Fax: 86-512-65371981